RECEPTION OF FILMS FROM POLYMER BLEND PVDF AND PABI

The solution spinning method was applied to preparation of polymeric films. In solution PABI brought powder PVDF in the ratio 1:1 (on weight) then added DMAA in quantity 2:1. The received mix

Heat uped to 80 0С and agitated during 10-15 mines for the purpose of removal of air traps from a mix.

A homogeneous solution poured out on bowl Petri and seated in a drying chamber for a solvent release and maintained to constant weight of a film [100-101].

At reception of composites the powder of powdery filler was brought in the received homogeneous solution in various percentage ratioes. Then a solution heat uped to 80 0С and agitated during 10 - 15 minutes poured out the Homogeneous solution a shallow layer on a glass and seated in a drying chamber where maintained at temperature 1400С, to constant weight of a film.

2.5.

<< | >>
A source: Danilov Anatoly Jurevich. OBTAINING POLYMERIC COMPOSITES WITH HIGH FERROELECTRIC AND THERMAL PROPERTIES. Thesis for the degree of candidate of chemical sciences. Tver - 2015. 2015

More on topic RECEPTION OF FILMS FROM POLYMER BLEND PVDF AND PABI:

  1. THE STRUCTURE OF FILMS FROM POLYMER BLEND PVDF AND PABI AND COMPOSITES ON ITS BASIS
  2. 4.3. SEGNETOELEKTRICHESKY PROPERTIES OF FILMS ON THE BASIS OF THE MATRIX FROM POLYMER BLEND PVDF AND PABI
  3. 4.4. SEGNETOELEKTRICHESKY PROPERTIES OF POLYMERIC COMPOSITES ON THE BASIS OF THE MATRIX FROM POLYMER BLEND PVDF AND PABI
  4. STRUCTURE of COMPOSITES ON THE BASIS OF POLYMER BLEND PVDF and PABI.
  5. THE STRUCTURE OF FILMS PABI AND COMPOSITES ON ITS BASIS
  6. THE STRUCTURE OF FILMS PVDF AND COMPOSITES ON ITS BASIS
  7. RECEPTION OF FILMS OF POLY(VINYLIDENE FLUORIDE)
  8. RECEPTION OF FILMS poliamidbenzimidazola
  9. Methods of reception of thin ferroelectric films TSTS
  10. termotropnyj mesomorphic polymer
  11. 1.4. ELECTRET PROPERTIES poliamidbenzimidazola (PABI)
  12. SEGNETOELEKTRICHESKY PROPERTIES PVDF AND COMPOSITES ON ITS BASIS
  13. STRUCTURE AND PROPERTIES OF POLY(VINYLIDENE FLUORIDE). LAWS OF OCCURRENCE SEGNETOELEKTRICHESTVA IN PVDF
  14. research of morphology of a film termotropnogo polymer
  15. thin films
  16. methods of making of films
  17. 2.1.2. Porous films of PE, software, PS
  18. loops of the dielectric hysteresis of films PZT